Injection molding plastic bonded hybrid NdFeB and ferrite magnets

type Remanence Maximum Energy Product Intrinsic Coercive Force Coercive Force Br (KG） (BH)max (MGOe) Hci (KOe) Hcb(min) (KOe) HGH-2 2.5-3.3 1.5-2.5 2.6-3.4 2.1-2.5 HGH-3 3.3-3.9 2.5-3.5 3.4-4.0 2.5-3.1 HGH-4 3.9-4.6 3.5-4.5 4.0-4.9 3.1-4.0 HGH-5 4.6-5.1 4.5-5.5 4.9-5.8 4.0-4.5 HGH-6 5.1-5.6 5.5-6.5 5.8-6.6 4.5-4.8 HGH-7 5.6-6.0 6.5-7.5 6.6-7.2 4.8-5.0 HGH-8 6.0-6.4 7.5-8.5 7.2-7.6 5.0-5.2 HGH-9 6.4-6.8 8.5-9.5 7.6-8.0 5.2-5.4 HGH-10 6.8-7.1 9.5-10.5 8.0-8.3 5.4-5.5 HGH-11 7.1-7.4 10.5-11.5 8.3-8.6 5.5-5.6 HGH-12 7.4-7.6 11.5-12.5 8.6-8.8 5.6-5.8 HGS-4 4.3-4.8 4.0-4.5 7.7-8.7 3.4-3.9 Notes : The properties given above are typical at room temperature (23oC) for coated samples.

Compression molding epoxy bonded isotropic NdFeB magnets

Type	Model	Remanence Br	Maximum Energy Product (BH)max	Intrinsic Coercive Force Hci	Coercive Force Hcb(min)	Density D	Temperature Coeffcient of Magnetic Induction α(25-100°C)	Temperature Coefficient of Coercive Force β(25-100°C)
		mT (KG）	KJ/m3 (MGOe)	KA/m (KOe)	KA/m (KOe)	g/cm3	(%/°C)	(%/°C)
High remanence	HC-B	660-700 6.6-7.0	69.6-80.0 8.7-10.0	640-720 8.0-9.0	392 4.9	6.0	-0.11	-0.40
	HC-B+	680-710 6.8-7.1	76.8-84.0 9.6-10.5	720-800 9.0-10.0	440 5.5	6.0	-0.11	-0.41
High Coercive Force	HC-A	590-640 5.9-6.4	60.0-68.0 7.5-8.5	1040-1200 13.0-15.0	400 5.0	6.0	-0.12	-0.38
	HC-A1	600-640 6.0-6.4	64.0-72.0 8.0-9.0	1040-1120 13.0-14.0	400 5.0	6.0	-0.12	-0.40
	HC-C	590-620 5.9-6.2	60.0-68.0 7.5-8.5	1200-1360 15.0-17.0	400 5.0	6.0	-0.07	-0.42
High stability	HC-D	640-6806.4-6.8	70.4-76.0 8.8-9.5	720-800 9.0-10.0	432 5.4	6.0	-0.08	-0.39
	HC-O	600-640 6.0-6.4	61.6-68.0 7.7-8.5	880-1040 11.0-13.0	416 5.2	6.0	-0.13	-0.37
	HC-14-12	640-970 6.4-6.7	68.0-73.6 8.5-9.2	880-104011.0-13.0	440 5.5	6.0	-0.14	-0.37
Magnetizable	HC-15-7	680-740 6.8-7.4	75.2-88.0 9.4-11	520-560 6.5-7.0	400 5.0	6.0	-0.11	-0.39
	HC-16-7	710-770 7.1-7.7	80.0-96.0 10.0-12.0	536-576 6.7-7.2	424 5.3	6.0	-0.08	-0.52
Normal	HC-13-9	600-640 6.0-6.4	60.8-68.0 7.6-8.5	640-720 8.0-9.0	400 5.0	6.0	-0.12	-0.43
	HC-M11	620-670 6.2-6.7	56.0-64.0 7.0-8.0	680-760 8.5-9.5	368 4.6	6.0	-0.12	-0.43
	HC-L9	600-650 6.0-6.5	48.0-56.0 6.0-7.0	640-720 8.0-9.0	336 4.2	6.0	-0.12	-0.43
Notes : The properties given above are typical at room temperature (23oC) for coated samples.

Injection molding plastic bonded ferrite magnets

Just Remanence Br The largest magnetic energy (BH)max Far edge of the natural reconstruction Hci Dissemble seek edge Hcb Magnetic flu temperature coefficient α(25-100) Dissemble far edge temperature coefficient α(25-100) mT KJ/m3(MGOe) KA/m KA/m °C °C 176 2.2 260 2.60 13.2 1.65 264 3.3 192 2.4 272 2.72 14.4 1.8 232 2.9 192 2.4 287 2.87 16.0 2.0 208 2.6 188 2.35 285 2.85 16.1 2.01 216 2.7 192 2.4 290 2.90 16.4 2.05 232 2.9 200 2.5 292 2.92 16.6 2.07 228 2.85 200 2.5 300 3.0 17.6 2.2 228 2.85 204 2.55 Notes : magnetic parameters at room temperature to (23oC), the measurement of magnetic data acquired